1414 Spun Aramid Fiber For High Temperature Resistant Non-Woven Fabric, Industrial Felt, Spinning

1414 Spun Aramid Fiber For High Temperature Resistant Non-Woven Fabric, Industrial Felt, Spinning


Description

Brand: SFFILTECH

Place of Origin: China

Fiber morphology: Spun

Product Name: Aramid 1414 staple fiber

Main raw material: Aramid fiber

Color: yellow

Can it be customized: yes.

Main purpose: Non-woven fabric textile yarn filter material, industrial weaving and engineering fiber

Type: Spun

Aramid chopped yarn is cut from Aramid filament by chopping equipment according to certain specific length requirements.

Aramid 1414 staple fiber is made of aramid 1414 filament which is curled and cut. The linear density is 1.5D ~ 2.5D and the length ranges between 38mm, 51mm, 65mm and 76mm.

The other specifications are;

It is an organic fiber with ultra-high strength

.high modulus

.high temperature resistance

.acid and alkali resistance

.light weight

.It has good dimensional stability at high temperature

.wear and heat resistance

. Aramid chopped fiber to a certain extent solves the problem better than aramid pulp which is not easy to loosen and disperse as well as is not easy to pill and form fiber clusters . Aramid chopped fiber reduces noise, reduces the wear of drums and discs and has obvious high efficiency and performance.

Main features:

1. Aramid high-temperature fire-proof wire has extremely high strength. Its weight specific tensile strength is 6 times that of steel wire, 3 times that of glass fiber, and 2 times that of high-strength nylon industrial wire.

2. The tensile modulus of aramid fireproof wire is 3 times that of steel wire, 2 times that of glass fiber, and 10 times that of high-strength nylon industrial wire.

3. The continuous use temperature range of aramid fire-proof wire is extremely wide. It ranges from 196℃ and can operate normally for a long time within the range of 204 °C. The shrinkage is 0% at 150 ℃ and it will not melt at 560℃.

4. Mechanical properties:

Strength: 3.6 GPA

Elongation modulus: 131 GPA

Elongation at break: 2.8

Main features:

1. Aramid high-temperature fire-proof wire has extremely high strength. Its weight specific tensile strength is 6 times that of steel wire, 3 times that of glass fiber, and 2 times that of high-strength nylon industrial wire.

2. The tensile modulus of aramid fireproof wire is 3 times that of steel wire, 2 times that of glass fiber, and 10 times that of high-strength nylon industrial wire.

3. The continuous use temperature range of aramid fire-proof wire is extremely wide. It ranges from 196℃ and can operate normally for a long time within the range of 204 °C. The shrinkage is 0% at 150 ℃ and it will not melt at 560℃.

4. Mechanical properties:

Strength: 3.6 GPA

Elongation modulus: 131 GPA

Elongation at break: 2.8

Outstanding features:

It has the advantages of high temperature resistance, fire resistance, light weight, high strength, high modulus, stable size, low shrinkage, puncture resistance, cutting resistance, wear and tear resistance, heat resistance, chemical corrosion resistance, good mechanical properties, good dielectric properties etc.

It is used in the fields of high temperature resistant non-woven fabric, industrial felt, spinning, core spun yarn and anti-cutting.